Michimid K4100GFMN40
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | API Polymers, Inc. |
| Trademark: | Michimid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gEGg7d_Michimid-K4100GFMN40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Michimid K4100GFMN40 is a Polyamide 6 (Nylon 6) product filled with 40% glass\mineral. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 110 | MPa | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 175 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | ASTM D789 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 266 | °C | |
| Front Temperature | 266 | °C | |
| Nozzle Temperature | 266 | °C | |
| Processing (Melt) Temp | 282 | °C | |
| Mold Temperature | 79.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylex™ 1230 | Multibase, A Dow Corning Company | Nylon+PP | Nylex™ |
| Akulon® Diablo HT-HG0 (K-X07029) | DSM Engineering Plastics | Nylon 66/6 | Akulon® |
| DJSilicone NE-171 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Sylvin 6238-75 Red 6302 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Geon™ Vinyl Flexible HC27000G | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |