POLYFORT® FPP 1005
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | POLYFORT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e3Qp2V_POLYFORT-FPP-1005.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP Modified 40% Talc |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 1 | 0.80 | % | Internal Method |
| Vinyl Acetate Content | 3.0 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 32.0 | MPa | ASTM D638 |
| Flexural Modulus 3 | 3600 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 20 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 105 | °C | |
| 1.8 MPa, Unannealed | 60.0 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 41 | % | ASTM D5630 |
| Note Message | |
|---|---|
| 1 . | 5x7 in plaque |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tisoplen® PPC 20 MNF CALCITE | Tisan | PP Copolymer | Tisoplen® |
| OmniPro™ HPP GMR20 WS02 BK1000 | OMNI Plastics, LLC | PP Homopolymer | OmniPro™ |
| PHOENIX™ 7652 | Phon Tech Industrial Company | TPE | PHOENIX™ |
| Sylvin 7868-80 White 1118 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 3240-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |