3M™ Dyneon™ Fluoroelastomer FE 5830Z

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ Fluoroelastomer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	g38upZ_3MDyneonFluoroelastomerFE5830Z.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
3M™ Dyneon™ Fluoroelastomer FE 5830Z is a terpolymer made from hexafluoropropylene, vinylidene fluoride and tetrafluoroethylene. FE 5830Z has an incorporated bisphenol cure system. Special Features Composition: terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene Process targets: Extrusion only. Not recommended for moulded goods application Can be formulated to yield good permeation resistance to automotive fuels High fluorine extrusion grade Produces smooth extrudates without the use of processing aids Proprietary incorporated cure technology Can be formulated to meet -40°C mandrel bend fuel hose specifications Typical Applications 3M™ Dyneon™ Fluoroelastomer FE 5830Z is suitable for hoses for the entire fuel system.

Message

3M™ Dyneon™ Fluoroelastomer FE 5830Z is a terpolymer made from hexafluoropropylene, vinylidene fluoride and tetrafluoroethylene. FE 5830Z has an incorporated bisphenol cure system.

Special Features

Composition: terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene

Process targets: Extrusion only. Not recommended for moulded goods application

Can be formulated to yield good permeation resistance to automotive fuels

High fluorine extrusion grade

Produces smooth extrudates without the use of processing aids

Proprietary incorporated cure technology

Can be formulated to meet -40°C mandrel bend fuel hose specifications

Typical Applications
3M™ Dyneon™ Fluoroelastomer FE 5830Z is suitable for hoses for the entire fuel system.

General Information
Features	Terpolymer
Uses	Pipe Fuel line
Appearance	Opacity White-like
Forms	Thick sheet
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.89	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	36	MU	Internal method
Fluorine Content	70	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	73		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	4.30	MPa	ASTM D412A
Tensile Strength ²	11.5	MPa	ASTM D412A
Tensile Elongation ³(Break)	240	%	ASTM D412A
Compression Set ⁴(200°C, 70 hr)	44	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould
4 .	Post cured 2 hours @ 180°C

Resin Grade	Manufacturer	Category	Trademark
Premi-Glas® 1203-28	Premix, Inc.	TS, Unspecified	Premi-Glas®
AKROMID® A3 GF 35 S1 black (2717)	AKRO-PLASTIC GmbH	Nylon 66	AKROMID®
ALCUDIA® LDPE 3235FG	REPSOL	LDPE	ALCUDIA® LDPE
Hangzhou Jinxin VMPET Film for Metallic Yarn/Glitter Powder	Hangzhou Jinxin Filming Packaging Co., Ltd.	Film, PET	Hangzhou Jinxin
SABIC® LDPE 2402CX0	Saudi Basic Industries Corporation (SABIC)	LDPE	SABIC® LDPE