SABIC® PP CX02-82
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | flEPKR_SABIC-PP-CX02-82.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP CX02-82 is an emission optimised high crystalline copolymer. It offers high stiffness, in perfect balance with high thermal dimensional stability, impact resistance and flow. This material has excellent aesthetic properties as well and is typically used for automotive interior applications. It is the obvious alternative to conventional talc-filled copolymers, offering considerable weight saving advantage. SABIC® PP CX02-82 is a designated automotive grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 24 hr | 1.6 | % | |
| 24 hr | 1.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant : Injection Molded 1 | 1600 | MPa | ASTM D638 |
| Injection Molded | 1550 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, Injection Molded 2 | 26.0 | MPa | ASTM D638 |
| Yield, Injection Molded | 27.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield, Injection Molded 3 | 4.0 | % | ASTM D638 |
| Yield, Injection Molded | 4.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C, Injection Molded | 8.0 | kJ/m² | |
| 23°C, Injection Molded | 13 | kJ/m² | |
| Notched Izod Impact | |||
| -20°C, Injection Molded | 70 | J/m | ASTM D256A |
| 0°C, Injection Molded | 75 | J/m | ASTM D256A |
| 23°C, Injection Molded | 100 | J/m | ASTM D256A |
| -20°C, Injection Molded | 6.0 | kJ/m² | ISO 180/1A |
| 0°C, Injection Molded | 7.0 | kJ/m² | ISO 180/1A |
| 23°C, Injection Molded | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 151 | °C | ASTM D1525, ISO 306/A120 4 4 |
| -- | 80.0 | °C | ASTM D1525, ISO 306/B120 5 5 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Carbon Emission | < 50.0 | µg/g | VDA 277 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | Rate B (120°C/h), Loading 1 (10 N) |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AMTOPP VS30 | Inteplast Group | PP, Unspecified | AMTOPP |
| Colorite CS Series CS1533UL | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| ColorFast® GPA100 | LTL Color Compounders, Inc. | ABS | ColorFast® |
| HIDEN® M830 | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |
| INELEC PE | Infinity LTL Engineered Compounds | HDPE | INELEC |