| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | Guarniflon S.p.A. - Flontech Division |
| Trademark: | Flontech® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ivu35v_Flontech-FT-BRR40-8.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| 38-42% bronze + 58-62% PTFE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 3.08 | g/cm³ | ASTM D4894 |
| Apparent Density | 0.85 | g/cm³ | ASTM D4894 |
| Average Particle Size | 300 | µm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 36 | ASTM D785 | |
| Durometer Hardness (Shore D) | 59 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength - Across Flow (1.00 mm) | 14.0 | MPa | ASTM D4894 |
| Tensile Elongation - Across Flow (Break, 1.00 mm) | 170 | % | ASTM D4894 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO AES W245 | Techno Polymer Co, Ltd. | AES | TECHNO AES |
| SPESIN® KP212G30V0HI | Kolon Plastics, Inc. | PBT | SPESIN® |
| Emulprene® 1011CR | INSA | SBR, Emulsion | Emulprene® |
| Karina GRAY PVC COMPOUND 700-DA-18/291-Y-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ RF0049S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |