Evoprene™ GC 920
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Mexichem Specialty Compounds Inc. |
| Trademark: | Evoprene™ GC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ficdHz_EvopreneGC920.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Non black dynamic . Window gasket. |
| General Information | |
|---|---|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shaw A, 10 seconds, 6.50mm) | 62 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain, 2.00 mm) | 1.80 | MPa | ISO 37 |
| Tensile Stress (Yield, 2.00 mm) | 6.20 | MPa | ISO 37 |
| Tensile Elongation (Break, 2.00 mm) | 610 | % | ISO 37 |
| Tear Strength 1(2.00 mm) | 28 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 22°C, 72 hr | 21 | % | ISO 815 |
| 70°C, 22 hr | 59 | % | ISO 815 |
| 100°C, 22 hr | 77 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (70°C, 336 hr) | 4.0 | % | ISO 188 |
| Change in Tensile Strain at Break in Air (70°C, 336 hr) | 2.0 | % | ISO 188 |
| Change in Shore Hardness in Air (Shao A, 70°C, 336 hr) | 0.0 | ISO 188 |
| Additional Information |
|---|
| The value listed as Density, ISO 1183, was tested in accordance with ISO 2782 test methods.Abrasion, DIN 53516: 145 mm³M-S, Alpha Gary Test Method: 13 kg/cm²M-S (Macklow Smith) flow measures force to extrude tape through die 10mm X 1mm. The higher the value the stiffer the flow (opposite to Melt Flow - MFI)Service Temperature: -50 to +120°COzone Resistance, 100 pphm, 200hrs, 20% strain, 35°C: No cracksOK for food contact: NoThermoplastic Compatability: PP |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (without cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCLAIR® 2908 | NOVA Chemicals | HDPE | SCLAIR® |
| TECHNAMID® A A-SV25-ETK | Poly Plastic | Nylon 66 | TECHNAMID® A |
| Sindustris PC GN5008FL | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| 3M™ Dyneon™ PTFE Compound TF 6221 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Fainplast PVC RH 4410 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |