Tecnoprene® 3K6 NERO903
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Tecnoprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fglIFm_Tecnoprene-3K6-NERO903.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene copolymer reinforced with 30% chemically coupled glass fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.50 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Ash Content | 30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 75.0 | MPa | ASTM D638 |
| Flexural Modulus | 5600 | MPa | ASTM D790 |
| Flexural Strength | 115 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 120 | J/m | |
| 23°C | 160 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 146 | °C | ASTM D648 |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Dielectric Constant (1 kHz) | 2.50 | ASTM D150 | |
| Comparative Tracking Index | 650 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 210 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 287B | RTP Company | Nylon 610 | RTP |
| TAFMER™ A-4050S | Mitsui Chemicals America, Inc. | PAO | TAFMER™ |
| Nycal™ 2150GB40 | Technical Polymers, LLC | Nylon 66 | Nycal™ |
| DJSilicone NE-G131 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| GLS 287-094 | PolyOne Corporation | TPE | GLS |