Ferro PP NPP99GB02AL
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fCDau5_Ferro-PP-NPP99GB02AL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ferro PP NPP99GB02AL is a Polypropylene material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.908 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 22.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 200 | % | ASTM D638 |
| Flexural Modulus | 931 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 27.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Gardner Impact (23°C) | 29.4 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 76.7 | °C | |
| 1.8 MPa, Unannealed | 48.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPR 3260 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| NYLOY® NS-0300N | Nytex Composites Co., Ltd. | Nylon 6 | NYLOY® |
| Eastar™ GN071, Natural | Eastman Chemical Company | Copolyester | Eastar™ |
| Elastron® D D100.A75.N | Elastron USA, Inc. | SBS | Elastron® D |
| MAJORIS PBT 9237 30 BV | AD majoris | PBT | MAJORIS |