Vi-Chem PVC V143-70E
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | Vi-Chem Corporation |
| Trademark: | Vi-Chem PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TEUQGh_Vi-Chem-PVC-V143-70E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vi-Chem PVC V143-70E is a Flexible Polyvinyl Chloride material. It is available in North America for extrusion. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 10.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 400 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | 30.0 | kN/m | ASTM D624 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (85°C, 1000 hr) | 0.10 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (85°C, 1000 hr) | 2.8 | % | ASTM D573 |
| Change in Mass in Air (85.0°C, 1000 hr) | 0.70 | % | ASTM D573 |
| Thermal | Nominal Value | ||
|---|---|---|---|
| Cold Flexibility (-34°C, 1.90 to 2.00 cm) | No cracking |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability | SE | ISO 3795 | |
| Fogging 3 | 76.0 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Soiling | < 3.4 | % |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | Die C, 500 mm/min |
| 3 . | FLTM BO116-03 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC1-1210 | Spartech Polycom | ABS | Spartech |
| PlexTuf 2000 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | PlexTuf |
| POLYfill PP CIP6015F | Polykemi AB | PP, Unspecified | POLYfill |
| LG EVA EA19400 | LG Chem Ltd. | EVA | LG EVA |
| 3M™ Dyneon™ PTFE Compound FC 100151000 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |