THERMOLAST® K TC4PCN (Series: AD/PA/CS)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | KRAIBURG TPE |
| Trademark: | THERMOLAST® K |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eZ1mle_THERMOLAST-K-TC4PCN-Series-AD-PA-CS-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The AD/PA/CS Series is your material solution for applications with excellent adhesion to PA as well as outstanding compression set. The compounds are available in natural and black colors. Typical applications
Material advantages
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 39 | ISO 7619 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(Yield) | 2.50 | MPa | ISO 37 |
| Tensile Elongation 2(Break) | 300 | % | ISO 37 |
| Tear Strength 3 | 9.0 | kN/m | ISO 34-1 |
| Compression Set 4 | ISO 815 | ||
| 23°C, 72 hr | 14 | % | |
| 70°C, 24 hr | 31 | % | |
| 100°C, 24 hr | 43 | % |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Adhesion to PA6 | 8.0 | kN/m | Renault D41/1916 |
| Adhesion to PA66 | 5.0 | kN/m | Renault D41/1916 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 230 to 245 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Pressure | 20.0 to 100 | MPa | |
| Back Pressure | 2.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Type S2, 200 mm/min |
| 2 . | Type S2, 200 mm/min |
| 3 . | Method Bb, Angle (Nicked) |
| 4 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Kepital® TC3020 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| LightSpan® LS-3354 | NuSil Technology | Silicone | LightSpan® |
| PermaStat PLUS® 2500 A | RTP Company | PC+ABS | PermaStat PLUS® |
| SD POLYCA™ CR3441 | Sumika Styron Polycarbonate Limited | PC+PBT | SD POLYCA™ |
| VALOX™ 420SE0 resin | SABIC Innovative Plastics | PBT | VALOX™ |