Next Nylon 66 Prime Series PGF30-01NC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eQYZ6v_Next-Nylon-66-Prime-Series-PGF30-01NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 Glass Fiber Reinforced FR Natural Compound Product Applications This product is ideally suited for Appliances, Industrial control, Power distribution application such as MCCB and Connectors. The long term thermal performance of this grade also make it ideal for under- the -Bonnet Auto application where it can withstand temperature of 160 Deg. °c for over 6000 Hrs. Benefits This Halogen & Red phosphorous Free flame retardent grade combines excellent mechanical properties with outstanding flame retardency and Electrical performance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.46 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.30 | -- | % | |
| Across Flow | 0.80 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 0.73 | -- | % | |
| Saturation 1 | 5.6 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 110 | -- | ||
| R-Scale | 125 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11700 | 8400 | MPa | ASTM D638 |
| Tensile Strength | 150 | 115 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 5.0 | % | ASTM D638 |
| Flexural Modulus | 9500 | 7800 | MPa | ASTM D790 |
| Flexural Strength | 210 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 74 | 98 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 260 | -- | °C | |
| 1.8 MPa, Unannealed | 245 | -- | °C | |
| Melting Temperature | 263 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 32 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-0 | -- | ||
| 1.60 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.60 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.800 mm | 775 | -- | °C | |
| 1.60 mm | 775 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene TPP1040 | Teknor Apex Asia Pacific PTE. LTD. | PP Homopolymer | Sinpolene |
| UNISOFT TPE™ ST-40A-CL-1-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| BIOPLAST® 105 | BIOTEC GmbH & Co. KG | TP, Unspecified | BIOPLAST® |
| ASTATAL™ FV30 | Marplex Australia Pty. Ltd. | Acetal (POM) Homopolymer | ASTATAL™ |
| ESTOPLAST EP 4030GY27 | Ester Industries Ltd. | PBT | ESTOPLAST EP |