Durethan® B 30 S F30 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FcBh26_Durethan-B-30-S-F30-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, non-reinforced, injection molding, flame retardant |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow : 260°C, 2.00 mm 1 | 1.1 | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.40 | % | |
| Flow : 260°C, 2.00 mm 3 | 1.1 | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 70.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 3.7 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 9.0 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 3200 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | ||
| 3.5% Strain, 23°C | 100 | MPa | |
| 23°C 6 | 110 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 5.5 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA 6, GFHR, 14-040; ISO 1043-PA FR (17) | ISO 1874 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Admissible Residence Time at Tmax | > 10.0 | min | |
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 130 | kJ/m² | |
| 23°C | 150 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 100 | kJ/m² | |
| 23°C | 120 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 70.0 | °C | ISO 75-2/A |
| Melting Temperature 8 | 222 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-0 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | 5VA | ||
| 3.00 mm | 5VA | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 960 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 825 | °C | |
| 1.50 mm | 825 | °C | |
| 3.00 mm | 800 | °C |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SZF4569 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Spartech Polycom PP6113 A67 | Spartech Polycom | PP, Unspecified | Spartech |
| Supol HP908E | LyondellBasell Industries | PP Copolymer | Supol |
| LEXAN™ 103 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LNP™ LUBRICOMP™ Lexan_LF1510A compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |