TECACOMP® PK TRM PVX black 4180
| Category: | PK , Polyketone |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eMLDTO_TECACOMPPKTRMPVXblack4180.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (240°C/2.16 kg) | 21 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (240°C/2.16 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.1 | % | ISO 294-4 |
| Flow | 0.60 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5800 | MPa | ISO 527-2 |
| Tensile Stress | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 207 | °C | ISO 75-2/A |
| Glass Transition Temperature | 15.0 | °C | DIN 53765 |
| Melting Temperature | 220 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 1 | 0.38 | W/m/K | DIN EN 821 |
| -- 2 | 0.65 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| long term | 100 | °C | |
| short term | 140 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.9E+4 | ohms | DIN EN 61340 |
| Volume Resistivity | 2.4E+6 | ohms·cm | DIN EN 61340 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Processing (Melt) Temp | 220 - 250 | °C | |
| Mold Temperature | 120 | °C |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ABS TR-2 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| VECTOR® 4213A | Dexco Polymers LP | SIS+SI | VECTOR® |
| Desmopan® 385 E | Covestro - PUR | TPU-Polyester | Desmopan® |
| Fainplast PVC GK 77/R1 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| EXTEM™ VH1003M resin | SABIC Innovative Plastics Asia Pacific | PEI | EXTEM™ |