CALIBRE™ 302EP-22
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eHyTaE_CALIBRE-302EP-22.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 300EP-22 Series are polycarbonate resins that offer exceptional impact resistance, heat distortion resistance, and optical clarity for injection molding applications. Their high melt flow rate allows complex parts to be easily molded. The CALIBRE 300EP-22 series products are available in 4 additive packages: CALIBRE 300EP: No mold release or UV Stabilizer. CALIBRE 301EP: Mold release. CALIBRE 302EP: UV stabilizer. CALIBRE 303EP: Mold release and UV stabilizer. Govt. and Industry Standards:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 22 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 73 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2340 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break 3 | 65.5 | MPa | ASTM D638 |
| Break | 65.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 120 | % | ASTM D638 |
| Break | 120 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 6 | 2410 | MPa | ASTM D790 |
| -- 7 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 8 | 96.5 | MPa | ASTM D790 |
| -- 9 | 97.0 | MPa | ISO 178 |
| Taber Abrasion Resistance | 45 | % | ASTM D1044 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Average Extent of Burning | 3 | cm | ASTM D635 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 750 | J/m | ASTM D256 |
| 23°C | 74 | kJ/m² | ISO 180/A |
| Instrumented Dart Impact 10(23°C, Total Energy) | 72.3 | J | ASTM D3763 |
| Tensile Impact Strength | 378 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 142 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 126 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 122 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 139 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 147 | °C | ISO 306/B50, ASTM D1525 11 |
| Ball Indentation Temperature | 125 | °C | IEC 60335-1 |
| CLTE - Flow (-40 to 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.0E-3 | ||
| 1 MHz | 2.0E-3 | ||
| Comparative Tracking Index (2.00 mm, Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 12 | UL 94 | ||
| 1.59 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Oxygen Index 13 | 26 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542, ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | Type I, 51 mm/min |
| 5 . | Type I, 51 mm/min |
| 6 . | Method I (3 point load), Type I, 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | Method I (3 point load), Type I, 2.0 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 3.39 m/sec |
| 11 . | Rate A (50°C/h), Loading 2 (50 N) |
| 12 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 13 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® PE 1294 | Premix Oy | HDPE | PRE-ELEC® |
| YUCLAIR® FG450 | SK Global Chemical | LLDPE | YUCLAIR® |
| Fiberfil® J-60/30/E4 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Geon™ Vinyl Rigid Extrusion L0676 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Ipethene® 100 | Carmel Olefins Ltd. | LDPE | Ipethene® |