ResMart Repro Nylon 6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | ResMart |
| Trademark: | ResMart Repro |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | e6Ddif_ResMart-Repro-Nylon-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 6 produced from reprocessed industrial feedstocks that offers a robust and economical property set |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Moisture Content | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 55.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 1100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 168 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 82.2 | °C | |
| Drying Time - Desiccant Dryer | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 243 - 279 | °C |
| Injection instructions |
|---|
| Dew Point: 0°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Solprene® 416 | Dynasol Elastomers | SBS | Solprene® |
| SUNFROST® KD90EA | Mitsubishi Chemical Performance Polymers, Inc. | PVC Elastomer | SUNFROST® |
| MORETEC™ 0218CM | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| NuSil R-2200-11 | NuSil Technology | Silicone | NuSil |
| Geon™ Vinyl Flexible R267AM | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |