DOW™ LDPE 525E

Category:	LDPE , Low Density Polyethylene Resin
Manufacturer:	The Dow Chemical Company
Trademark:	DOW™ LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	dalD9M_DOW-LDPE-525E.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
DOW LDPE 525E low density polyethylene resin is easy to process using common blow film technology, and the melt temperature range is 160 to 195°C. When prepared, this resin has excellent mechanical properties, and can maintain stability even when its density is high (high stiffness) compared with standard resins, while maintaining very high transparency and gloss. It has good drafting performance and processing performance. The product does not contain slip agent or anti-blocking agent. Note: When applied to the application field of contact food, DOW LDPE 525E low density polyethylene should comply with U.S. Food and Drug Administration Regulations 21 CFR 177.1520(c)2.2, EU, No 10/2011 without modification and when the processing process follows the requirements of good manufacturing practices. Please contact your nearest Dow representative for proof of compliance with the Food Contact Act. The purchaser remains responsible for determining whether the use of its products complies with all relevant regulations. Application field: high transparency composite film label film packaging of soft items, such as facial tissue, toilet paper, women's hygiene products, etc. high transparency paper towel packaging film fresh food packaging bag food packaging film

Message

DOW LDPE 525E low density polyethylene resin is easy to process using common blow film technology, and the melt temperature range is 160 to 195°C. When prepared, this resin has excellent mechanical properties, and can maintain stability even when its density is high (high stiffness) compared with standard resins, while maintaining very high transparency and gloss. It has good drafting performance and processing performance. The product does not contain slip agent or anti-blocking agent.

Note: When applied to the application field of contact food, DOW LDPE 525E low density polyethylene should comply with U.S. Food and Drug Administration Regulations 21 CFR 177.1520(c)2.2, EU, No 10/2011 without modification and when the processing process follows the requirements of good manufacturing practices. Please contact your nearest Dow representative for proof of compliance with the Food Contact Act. The purchaser remains responsible for determining whether the use of its products complies with all relevant regulations.

Application field:

high transparency composite film

label film

packaging of soft items, such as facial tissue, toilet paper, women's hygiene products, etc.

high transparency paper towel packaging film

fresh food packaging bag

food packaging film

General Information
Agency Ratings	FDA 21 CFR 177.1520(c) 2.2 Europe No 10/2011
Forms	Particle
Processing Method	Blow film

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.930	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	3.2	g/10 min	ISO 1133

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	50	µm
Tensile Modulus			ISO 527-3
2% secant, MD : 50 µm	290	MPa	ISO 527-3
2% secant, TD : 50 µm	250	MPa	ISO 527-3
Tensile Stress			ISO 527-3
MD : Yield, 50 µm	15.0	MPa	ISO 527-3
TD : Yield, 50 µm	14.0	MPa	ISO 527-3
MD : Break, 50 µm	19.0	MPa	ISO 527-3
TD : Break, 50 µm	14.5	MPa	ISO 527-3
Tensile Elongation			ISO 527-3
MD : Break, 50 µm	440	%	ISO 527-3
TD : Break, 50 µm	530	%	ISO 527-3
Dart Drop Impact (50 µm)	85	g	ISO 7765-1/A
Elmendorf Tear Strength			ASTM D1922
MD : 50 µm	240	g	ASTM D1922
TD : 50 µm	180	g	ASTM D1922

Extrusion	Nominal Value	Unit
Melt Temperature	160 - 195	°C

Extrusion instructions
放大比 1:2.5

Resin Grade	Manufacturer	Category	Trademark
Ravamid® R200 GB 30	Ravago Group	Nylon 6	Ravamid®
Purell HP570M	LyondellBasell Industries	PP Homopolymer	Purell
Network Polymers PP PPB 25 0202	Network Polymers, Inc.	PP Copolymer	Network Polymers PP
FM® 2555	Cytec Industries Inc.	Adhesive	FM®
OmniLon™ PA6/6 MF20	OMNI Plastics, LLC	Nylon 66	OmniLon™