PP ABS AF312C
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Performance Plastics, Ltd. |
| Trademark: | PP ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | daVfUv_PP-ABS-AF312C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AF-312C is specifically engineered to meet the need for high performance products in the flame retardant resin applications. AF-312C provides an optimum balance of physical properties, high heat resistance,outstanding UV stability and good finished part aesthetics. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 5.1 | g/10 min | |
| 220°C/10.0 kg | 53 | g/10 min | |
| 230°C/3.8 kg | 17 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 22000 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 43.4 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 5.0 | % | |
| Break | 20 | % | |
| Flexural Modulus 4 | 27000 | MPa | ASTM D790 |
| Flexural Strength 5 | 71.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 78 | J/m | |
| -30°C, 6.40 mm | 78 | J/m | |
| 23°C, 3.20 mm | 280 | J/m | |
| 23°C, 6.40 mm | 250 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 88.0 | °C | |
| 0.45 MPa, Annealed, 6.40 mm | 83.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 76.0 | °C | |
| 1.8 MPa, Annealed, 6.40 mm | 84.0 | °C | |
| Vicat Softening Temperature | 84.0 | °C | ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP391H | Southern Polymer, Inc. | PP Impact Copolymer | PRIMALENE |
| TES J-1200/10/VO | Techmer Engineered Solutions | ABS | TES |
| ALTECH® PA6 A 1000/109 1129-12LS | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| LubriOne™ PC-000/05T Ice Green | PolyOne Corporation | PC | LubriOne™ |
| LEXAN™ HFD4211 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |