CERTENE™ LDF-420A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d7uPNb_CERTENE-LDF-420A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LDF-420A is a certified prime resin specially designed to meet the requirements of most 1 to 3 mils thickness Blown film liner applications. LDF-420A features easy processability. Large lot size and superior lot-to-lot uniformity ensure consistent film production. Minimum recommended film thickness is 1.0 mil. LDF-420A contains no slip and no antiblock. LDF-420A complies with FDA regulation 21CFR 177.1520 (c) 2.2 and with most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Film Thickness - Recommended / Available | Minimum 1.0 mil (25 µm) | ||
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm | 175 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm | 205 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm | 10.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm | 10.0 | MPa | ASTM D882 |
| MD : Fracture, 38 µm | 25.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 19.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 350 | % | ASTM D882 |
| TD : Fracture, 38 µm | 600 | % | ASTM D882 |
| Dart Drop Impact 1(38 µm) | 85 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 580 | g | ASTM D1922 |
| TD : 38 µm | 120 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 38.0 µm, Blown Film) | 10 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 5.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Specimen: 1.5 mils (38 µm) film, melt temperature 320-380°F (160-190°C), blow-up-ratio 2.25 :1. |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP TIVAR® PolySteel | Quadrant Engineering Plastic Products | UHMWPE | Quadrant EPP |
| SAPYLENE T25GF15HB | Sahel Chimie Co. | PP, Unspecified | SAPYLENE |
| Tecoform® PO20 GR25 NL HS | Eurotec Engineering Plastics | Acetal (POM) Copolymer | Tecoform® |
| Texalan® 2 Series 272D | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 2 Series |
| FINGERPRINT™ MDPE 7520 NT | The Dow Chemical Company | MDPE | FINGERPRINT™ |