POLYFLON™ F-208
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | DAIKIN AMERICA, INC. |
| Trademark: | POLYFLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OSApwI_POLYFLON-F-208.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daikin PTFE (polytetrafluoroethylene) fine powders are soft, white polymers that are produced from PTFE aqueous dispersions. These fine powders possess the lowest coefficient of friction, the highest heat resistance, chemical resistance, electrical properties, and non-sticking properties of all fluoropolymers. Daikin PTFE fine powders readily adsorb organic solvents resulting in the formation of a paste that can be easily extruded into thin, flexible sections. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density | 0.45 | g/cm³ | ASTM D4895 |
| Average Particle Size | 500 | µm | ASTM D4895 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Reduction Ratio 1 | > 4000 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | > 19.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 350 | % | JIS K6891 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 322 to 328 | °C | ASTM D4895 |
| Electrical | Nominal Value | ||
|---|---|---|---|
| Dielectric Constant | 2.10 | ||
| Dissipation Factor | 1.9E-4 |
| Note Message | |
|---|---|
| 1 . | The reduction ratio refers to the cross-sectional area of the resin nside the cylinder of the extruder (S1) and the cross-sectional area of the resin in the die land (S2), R. R. =S1/S2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Avalon 89 | Greene, Tweed & Co. | PTFE | Avalon |
| Fiberfil® M-2450 BK9083 | Fiberfil® Engineered Plastics Inc. | PP Copolymer | Fiberfil® |
| KOPLA PA66 KUG1330BK | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| Hylon® N1033THL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Karina IVORY PVC COMPOUND 807D35/ 1-C-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |