TOTAL Polypropylene PPC 10641
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cklgZs_TOTAL-Polypropylene-PPC-10641.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene PPC 10641 is a nucleated antistatic heterophasic copolymer with high Melt Flow Index of 44 g/10 min. Polypropylene PPC 10641 is characterized by high fluidity with good mechanical properties. Polypropylene PPC 10641 has been specially developed for high speed injection moulding of food packaging. We hereby confirm that we do not use peroxide in the manufacturing of the above-mentioned Product. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 44 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 1500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 4.5 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| -20°C | 4.0 | kJ/m² | |
| 23°C | 7.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 114 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 148 | °C | ISO 306/A50 |
| -- | 80.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® 8253 HS | BASF Corporation | Nylon 6 | Ultramid® |
| Aegis® H95XC | Honeywell | Nylon 6 | Aegis® |
| Formolene® 5140L | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| POLYFORT® FIPP 15 GFC BM K2258 | A. Schulman Europe | PP Copolymer | POLYFORT® |
| Hostacom HBC 386L G81523 | LyondellBasell Industries | PP Homopolymer | Hostacom |