INELEC TPUCF1050D
| Category: | TPU, Unspecified , Thermoplastic Polyurethane Elastomer |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INELEC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bvYvYG_INELEC-TPUCF1050D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INELEC TPUCF1050D is a Thermoplastic Polyurethane Elastomer product filled with 10% carbon fiber. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 to 0.30 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 48.3 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 25 | % | ASTM D638 |
| Flexural Modulus | 1170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 480 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 82.2 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 188 to 221 | °C | |
| Middle Temperature | 188 to 221 | °C | |
| Front Temperature | 188 to 221 | °C | |
| Processing (Melt) Temp | 210 | °C | |
| Mold Temperature | 15.6 to 65.6 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G0 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| NEXT REPROCESSED PA6 8202-300R | NEXT Specialty Resins, Inc. | Nylon 6 | NEXT REPROCESSED |
| HiFill® PA6 GF55 HS L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Petrothene® NA345013 | LyondellBasell Industries | LDPE | Petrothene® |
| LNP™ THERMOCOMP™ Lexan_LGK5030 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |