SABIC® LDPE 2308N0
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bvOgdd_SABIC-LDPE-2308N0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2308N0 is a LDPE tubular grade without additives. SABIC® LDPE 2308N0 is produced using SABIC Clean Tubular Reactor (CTR) Technology which ensure grades with high purity. It exhibits high toughness with good flexibility and reasonable environmental stress cracking resistance and is therefore typically used for flexibles and tough articles. Application
This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 7.5 | g/10 min | |
| 190°C/5.0 kg | 25 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 10.0 | cm³/10min | |
| 190°C/5.0 kg | 33.0 | cm³/10min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 41 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 170 | MPa | ISO 527-2/1A/50 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield, Injection Molded | 9.00 | MPa | |
| Break, Injection Molded | 10.0 | MPa | |
| Tensile Strain (Break, Injection Molded) | 100 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Injection Molded | 8.0 | kJ/m² | |
| 23°C, Injection Molded | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 46.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 110 | °C | DIN 53765 |
| Enthalpy Change | 138 | J/g | DIN 53765 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Forflex® 71600ID42 | SO.F.TER. SPA | TPO (POE) | Forflex® |
| Hanwha Total PP GB35F | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Keyflex® BT 3055D | LG Chem Ltd. | TPC-ET | Keyflex® BT |
| Hostacom TRC 364N C12752 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ LUBRICOMP™ DEL34E compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ LUBRICOMP™ |