Ultramid® A3WG7 HP BK20560
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aRyQpD_Ultramid-A3WG7-HP-BK20560.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid A3WG7 HP BK20560 is a 35% glass reinforced, heat stabilized, injection molding PA66 grade with excellent flow and surface finish. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.30 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 11200 | 8420 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 210 | 146 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.4 | 4.7 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 10000 | 7160 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 12 | 13 | kJ/m² | |
| 23°C | 15 | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 80 | 76 | kJ/m² | |
| 23°C | 95 | 100 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | |||
| -40°C | 12 | 13 | kJ/m² | |
| 23°C | 14 | 17 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 246 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAJORIS PP 30 FV NOIR 8229 | AD majoris | PP, Unspecified | MAJORIS |
| Taipol 6153 | TSRC Corporation | SEBS | Taipol |
| Sylvin 9715-60 Black | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| BJB Silicone TC-5030 A/B | BJB Enterprises, Inc. | Silicone | BJB Silicone |
| Cri-Line LC-612-THK | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |