LUVOCOM® 1200-8493 Datasheet,ABS,LEHVOSS Group-SHANGHAI SUSHENG

Message
LUVOCOM®1200-8493 is an acrylonitrile butadiene styrene (ABS) material containing stainless steel fibers. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main characteristics of 1200-8493 are: conductivity.

General Information
Filler / Reinforcement	Stainless steel fiber
Features	Conductivity Static conduction
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Molding Shrinkage	0.50 - 0.80	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.50	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3000	MPa	ISO 527-2
Tensile Stress (Break)	45.0	MPa	ISO 527-2
Tensile Strain (Yield)	2.5	%	ISO 527-2
Flexural Modulus	2500	MPa	ISO 178
Flexural Stress	65.0	MPa	ISO 178
Flexural Strain at Flexural Strength	3.0	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	80	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	25	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	60.0	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+4	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature - Desiccant Dryer	70 - 95	°C
Drying Time - Desiccant Dryer	2.0 - 4.0	hr
Rear Temperature	220 - 250	°C
Middle Temperature	220 - 250	°C
Front Temperature	230 - 260	°C
Nozzle Temperature	220 - 250	°C
Processing (Melt) Temp	230 - 260	°C
Mold Temperature	40 - 80	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.1%. Moisture may lead to smearing and in extreme cases to foaming. Usually the material can be processed over a broad temperature range and can thus be adapted to a wide variety of processing conditions. Temperatures >270°C may lead to thermal damage. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.1%. Moisture may lead to smearing and in extreme cases to foaming. Usually the material can be processed over a broad temperature range and can thus be adapted to a wide variety of processing conditions. Temperatures >270°C may lead to thermal damage. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	ABS , Acrylonitrile Butadiene Styrene
Manufacturer:	LEHVOSS Group
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	bmPdKm_LUVOCOM12008493.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TOTAL Polyethylene HDPE MS 201 BN-NA (EU)	TOTAL Refining & Chemicals	HDPE, HMW	TOTAL Polyethylene
Zhongfa PC FR2840G	Yuyao Zhongfa Engineering Plastics Co. Ltd.	PC	Zhongfa
Anjacom® 501-HI/UV	Almaak International GmbH	ABS	Anjacom®
HiPrene® MT43	GS Caltex	PP, Unspecified	HiPrene®
Elastoprene HS5150D NAT	KMI Group, Inc.	TPO (POE)	Elastoprene