| 15% GF PBT, Non-Brominated & Non-Chlorinated Flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/5.0 kg) | 24 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/5.0 kg | 17.0 | cm³/10min | |
| 265°C/5.0 kg | 18.0 | cm³/10min | |
| Molding Shrinkage - Flow 1 | 0.30 to 0.80 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.070 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 128 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 7300 | MPa | ASTM D638 |
| -- | 7500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 80.0 | MPa | ASTM D638 |
| Yield | 80.0 | MPa | ISO 527-2/5 |
| Break 4 | 80.0 | MPa | ASTM D638 |
| Break | 80.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 2.0 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/5 |
| Break 6 | 3.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 5800 | MPa | ASTM D790 |
| -- 8 | 6400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 130 | MPa | ISO 178 |
| Yield, 50.0 mm Span 9 | 120 | MPa | ASTM D790 |
| Break, 50.0 mm Span 10 | 120 | MPa | ASTM D790 |
| Flexural Strain at Break 11 | 3.0 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 15 | % | ASTM D229 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/2C | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/2U | ||
| -30°C | 25 | kJ/m² | |
| 23°C | 35 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 50 | J/m | ASTM D256 |
| 0°C | 50 | J/m | ASTM D256 |
| 23°C | 50 | J/m | ASTM D256 |
| -30°C 12 | 6.0 | kJ/m² | ISO 180/1A |
| 0°C 13 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 14 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 360 | J/m | ASTM D4812 |
| 23°C | 400 | J/m | ASTM D4812 |
| -30°C 15 | 23 | kJ/m² | ISO 180/1U |
| 23°C 16 | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 220 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 17 | 220 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 200 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 18 | 200 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 217 | °C | ASTM D1525 19 |
| -- | 205 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 20 |
| -- | 220 | °C | ISO 306/A50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.9E-5 | cm/cm/°C | |
| Flow : 23 to 150°C | 4.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | |
| Transverse : 23 to 150°C | 1.7E-4 | cm/cm/°C | |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | ASTM D149, IEC 60243-1 | ||
| 0.800 mm, in Oil | 28 | kV/mm | |
| 1.60 mm, in Oil | 21 | kV/mm | |
| 3.20 mm, in Oil | 17 | kV/mm | |
| Dielectric Constant (1 MHz) | 3.70 | ASTM D150, IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.15 | ASTM D150, IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (3.00 mm) | 750 | °C | IEC 60695-2-13 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C, 1500 sec^-1) | 150 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 235 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 230 to 255 | °C | |
| Processing (Melt) Temp | 245 to 260 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 2 mm/min |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 mm |
| 18 . | 80*10*4 mm |
| 19 . | Rate A (50°C/h), Loading 2 (50 N) |
| 20 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SWANCOR Epoxy 917 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| SUPREME HIPS SH 850 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| UBE Nylon 1022B | UBE Engineering Plastics, S.A. | Nylon 6 | UBE Nylon |
| NEFTEKHIM PP 1548R | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Hifax RTA3263UV | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |