LNP™ THERMOCOMP™ DX09309 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | bgGFHf_LNP-THERMOCOMP-DX09309-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP* THERMOCOMP* DX09309 is a mineral filled polycarbonate compound with high dielectric constant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.23 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.65 | % | |
| Across Flow : 3.20 mm | 0.56 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 27.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 4.2 | % | ASTM D638 |
| Flexural Modulus | 2490 | MPa | ASTM D790 |
| Flexural Strength | 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 68 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 94.0 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 6.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1.10 GHz) | 8.00 | Internal Method | |
| Dissipation Factor (1.10 GHz) | 0.010 | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 250 to 280 | °C | |
| Middle Temperature | 280 to 320 | °C | |
| Front Temperature | 280 to 320 | °C | |
| Nozzle Temperature | 280 to 320 | °C | |
| Processing (Melt) Temp | 280 to 320 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1205-70D TFE 20 | RTP Company | TPU-Polyester | RTP |
| Bergamid™ A70 MI40 H NC017 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| ExxonMobil™ AP3AW | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Karina ORANGE COLOR CONCENTRATE -E 32/ 34-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9604-95 Grey 930 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |