EcoPaXX® Q-KG6
| Category: | Nylon 410 , Polyamide 410 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | EcoPaXX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 71G2lh_EcoPaXX-Q-KG6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EcoPaXX® Q-KG6 is a Polyamide 410 (Nylon 410) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Important attributes of EcoPaXX® Q-KG6 are:
Typical application of EcoPaXX® Q-KG6: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.34 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.1 | -- | % | |
| Flow | 0.60 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | -- | % | ISO 62 |
| Calculated Bio-based Carbon Content | 70 | -- | % | ASTM D6866 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | 7000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 170 | 115 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 4.0 | 5.8 | % | ISO 527-2 |
| Flexural Modulus | 8500 | 6300 | MPa | ISO 178 |
| Flexural Stress | 260 | 185 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 9.0 | -- | kJ/m² | |
| 23°C | 11 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | -- | kJ/m² | |
| 23°C | 80 | 80 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 243 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 250 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 3.2E-5 | -- | cm/cm/°C | |
| Transverse | 6.6E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.5E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 2.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 40 | 35 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 300 | °C | |
| Processing (Melt) Temp | 275 to 310 | °C | |
| Mold Temperature | 80.0 to 140 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Royalstat R64 | Spartech Plastics | HDPE | Royalstat |
| Sindustris PP GP3210A | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Colorite CS Series CS7566LS | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| Flontech® FT-910-SH | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| ALCOM® PA66 910/1.1 CF40 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |