HiFill® PA6 0232 B
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZVieRk_HiFill-PA6-0232-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® PA6 0232 B is a Polyamide 6 (Nylon 6) product filled with barium sulfate. It can be processed by injection molding and is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 45.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 6340 | MPa | ASTM D790 |
| Flexural Strength | 49.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 174 | °C | |
| 1.8 MPa, Unannealed | 167 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 to 1.0E+14 | ohms·cm | ASTM D257 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLOX 111 G9 | Taro Plast S.p.A. | PET | TAROLOX |
| TRANSMARE® 10HT40-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| Cevian®-V SKG20 | Daicel Polymer Ltd. | ABS | Cevian®-V |
| ELIX™ Ultra 4105 | ELIX Polymers, S. L. | PC+ABS | ELIX™ Ultra |
| Lucent PBT GPB-FR515 | Lucent Polymers, Inc. | PBT | Lucent PBT |