NOVAPOL® PI-2024-A
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | NOVAPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b8LEtx_NOVAPOL-PI-2024-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Carrier resin for the following masterbatch applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.924 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 55 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, Compression Molded | 13.1 | MPa | |
| Break, Compression Molded | 8.96 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, Compression Molded | 12 | % | |
| Break, Compression Molded | 200 | % | |
| Flexural Modulus - 1% Secant (Compression Molded) | 415 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 91.1 | °C | ASTM D1525 |
| Melting Temperature | 122 | °C |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Wire & Cable GA-1021-CJ (All Colors) | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Wire & Cable |
| ALTECH® PA6 A 2045/500 GF45 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Borealis PP FSC65T30 | Borealis AG | TPO | Borealis PP |
| Hostacom PPU X9067HS C11498 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 6185-80 Red 6246 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |