Plaslube® PC-50/TF/13/SI/2
| Category: | PC , Polycarbonate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b4HZ8M_Plaslube-PC-50-TF-13-SI-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube®PC-50/TF/13/SI/2 is a polycarbonate (PC) product that contains fillers. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.27 | g/cm³ | ASTM D792 |
| -- | 1290 | kg/m³ | ISO 1183 1 |
| Molding Shrinkage - Flow (3.18 mm) | 0.70 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr | 0.12 | % | ASTM D570 |
| Saturation | 0.35 | % | ISO 62 2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2 3 |
| Tensile Stress | |||
| Yield | 50.0 | MPa | ISO 527-2 4 |
| 23°C | 48.3 | MPa | ASTM D638 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 5 |
| Tensile Elongation at Break | 40 | % | ISO 527-2 6 |
| Flexural Modulus (23°C) | 2000 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 72.4 | MPa | ASTM D790 |
| Compressive Strength | 62.1 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 136 | °C | ASTM D648 |
| 1.8 MPa | 130 | °C | ISO 75-2 7 |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 | |
| Burning Behav. at 1.6mm nom. thickn. (1.50 mm, UL) | HB | ISO 1210 8 |
| Additional Information |
|---|
| Compressive Strength, ASTM D695, 73°F: 9000 psi |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 299 - 316 | °C | |
| Middle Temperature | 310 - 327 | °C | |
| Front Temperature | 304 - 321 | °C | |
| Nozzle Temperature | 304 - 321 | °C | |
| Processing (Melt) Temp | 304 - 332 | °C | |
| Mold Temperature | 60.0 - 87.8 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well ventedMoisture Content, as received: Product is packaged at 0.2% or less. |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Texin® RxT50D | Covestro - PUR | TPU-Polyether | Texin® |
| NOVADURAN® 5810GN6-30 | Mitsubishi Engineering-Plastics Corp | PBT Alloy | NOVADURAN® |
| Formolene® E922 | Formosa Plastics Corporation, U.S.A. | HDPE, MMW | Formolene® |
| Petlon R-Prime B2-G30-00-BK | Petlon Polymers Ltd | Nylon 6 | Petlon R-Prime |
| SHINSTRA AG30TKB (PA6) | Shinil Chemical Industry Co., Ltd. | Nylon 6 | SHINSTRA |