LEXAN™ EX1632T resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0kGD9F_LEXAN-EX1632T-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN EX1632T polycarbonate resin, MVR (300C/1.2kg) 6 cm3/10min, high viscosity, branched, extrusion, mold release, UV stabilized, transparent, translucent and opaque colors. Multiwall sheet, Profiles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 300°C/1.2 kg | 6.00 | cm³/10min | |
| 300°C/2.16 kg | 11.0 | cm³/10min | |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 65.0 | MPa | |
| Break | 70.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 7.0 | % | |
| Break | > 70 | % | |
| Flexural Modulus 1 | 2300 | MPa | ISO 178 |
| Flexural Stress | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2 | ISO 179/1eA | ||
| -30°C | 50 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Charpy Unnotched Impact Strength 3 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| -30°C | 55 | kJ/m² | |
| 23°C | 75 | kJ/m² | |
| Unnotched Izod Impact Strength 5 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6(1.8 MPa, Unannealed, 64.0 mm Span) | 130 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ISO 306/B50 |
| -- | 150 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 7.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index (1.00 mm) | 850 | °C | IEC 60695-2-12 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Hopper Temperature | 100 to 120 | °C | |
| Cylinder Zone 1 Temp. | 240 to 270 | °C | |
| Cylinder Zone 2 Temp. | 240 to 270 | °C | |
| Cylinder Zone 3 Temp. | 240 to 270 | °C | |
| Adapter Temperature | 220 to 260 | °C | |
| Melt Temperature | 220 to 280 | °C | |
| Die Temperature | 220 to 280 | °C | |
| Calibration Temp, First | 50.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*3 sp=62mm |
| 3 . | 80*10*3 sp=62mm |
| 4 . | 80*10*3 |
| 5 . | 80*10*3 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4183 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| PRIMALENE WPP653G | Southern Polymer, Inc. | LLDPE | PRIMALENE |
| Santron IMS2000 | Bhansali Engineering Polymers Limited | SAN | Santron |
| DOWLEX™ 2645.01G | The Dow Chemical Company | LLDPE | DOWLEX™ |
| KEBATRON® PPS L2040G3 | BARLOG plastics GmbH | PPS | KEBATRON® |