RTV-2 GI-1000
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | Silicones, Inc. |
| Trademark: | RTV-2 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | b2zmsy_RTV-2-GI-1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GI-1000 is an extrememly high tear strength, tin-catalyzed RTV-2 silicone rubber, which was designed for casting polyester parts. GI-1000 is not sensitive to inhibition, meaning it will cure at room temperature over virtually any surface. It is easy to mix and de-air, and will cure with only a slight degree of shrinkage. The speed at which the rubber hardens can be accelerated with special activators. Condensation cure two-component silicone rubbers are excellent for most general mold making and prototype applications. They are excellent for casting waxes, gypsum, epoxies and other plastics. GI-1000 is extremely useful for those applications where superior mechanical properties are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | |
| Shrinkage - Cured | 0.10 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature - Cured | -51 to 177 | °C |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coverage - Cured | 0.918 | cm³/g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 1.0 Mix Ratio by Volume: 11 | ||
| Resin | Mix Ratio by Weight: 10 Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | 30000 to 45000 | cP |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Blue | ||
| -- 2 | White | ||
| Viscosity | |||
| -- 3 | 0.30 to 0.40 | Pa·s | |
| -- 4 | 50 to 70 | Pa·s | |
| Curing Time | 16 to 18 | hr | |
| Pot Life | 90 to 150 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | |||
| Shore A 5 | 24 to 32 | ||
| Shore A 6 | 28 to 36 | ||
| Tensile Strength | 3.45 to 3.62 | MPa | ASTM D412 |
| Tensile Elongation at Break | 280 to 330 | % | ASTM D412 |
| Tear Strength | 19.3 to 22.8 | kN/m | ASTM D624 |
| Electric Strength | 20 | kV/mm | |
| Relative Permittivity (100 Hz) | 3.30 | ||
| Volume Resistivity | 1.0E+15 | ohms·cm | |
| Dissipation Factor (100 Hz) | 0.019 |
| Note Message | |
|---|---|
| 1 . | Activator |
| 2 . | Base |
| 3 . | Activator |
| 4 . | Base |
| 5 . | 1 Day |
| 6 . | 7 Days |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® AGV HW 30 Black | Radici Plastics | Nylon 66 | Radilon® |
| STYRON™ 649D | Americas Styrenics LLC | PS (GPPS) | STYRON™ |
| Argothane® 19103 | Argotec LLC | TPU, Unspecified | Argothane® |
| Cellophane™ 400P23 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| POLYFLON™ M-532 | Daikin Fluorochemicals (China) Co., Ltd. | PTFE | POLYFLON™ |