LNP™ THERMOCOMP™ IF007 compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zrVgl6_LNP-THERMOCOMP-IF007-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* IF007 is a compound based on Nylon 6/12 resin containing 35% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound IF-1007 Product reorder name: IF007 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 8890 | MPa | ASTM D638 |
| Tensile Strength (Break) | 150 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 8270 | MPa | ASTM D790 |
| Flexural Strength | 228 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 800 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 199 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V932C NAT601AF | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SEETEC PP M1500 | LG Chem Ltd. | PP Impact Copolymer | SEETEC PP |
| XANTAR® RX 2124 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Lighter™ S98 | Equipolymers | PET | Lighter™ |
| Sylvin 4240-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |