SABIC® LLDPE 6118NE
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | azbl2t_SABIC-LLDPE-6118NE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LLDPE 6118NE is a hexene linear low density polyethylene resin. Films made from this resin exhibit an excellent tensile strength, stiffness, dart drop, impact strength, tear strength and seal/hottack properties. The suffix E denotes European origin. Typical application for SABIC® LLDPE 6118NE are heavy duty bags, lamination films, agriculture films, stretch wrap films, frozen food packaging and other applications requiring higher impact strength, high tear resistance and improved sealing properties. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, blown film | 190 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 230 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 11.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 12.5 | MPa | ISO 527-3 |
| MD : Broken, 50 µm, blown film | 47.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 40.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 630 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 800 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown Film (50.0 µm) | 350 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance - Blown Film (50.0 µm) | 750 | J/m | Internal method |
| Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 100.0 | kN/m | ISO 6383-2 |
| TD : 50.0 µm | 400.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 106 | °C | ISO 306/A |
| Melting Temperature (DSC) | 124 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 57 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 13 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film of 50 µm and BUR = 2 has been produced on Kiefel IBC with 140 kg/h. Die size 200 mm, die gap 2.7 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8983-90 White 1196 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Tritan™ MX711 | Eastman Chemical Company | Copolyester | Tritan™ |
| AKROMID® B3 GF 10 natural (2829) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Petrotene® PP A3 G40 HF CNZ0207 PH356 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |
| Sylvin 9950-60 Red 6175 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |