LNP THERMOCOMP KF006XXC is a compound based on Acetal Copolymer resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound KF-1006 Product reorder name: KF006XXC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.50 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.6 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.6 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.49 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11000 | MPa | ASTM D638 |
| -- | 10400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 116 | MPa | ASTM D638 |
| Yield | 121 | MPa | ISO 527-2 |
| Fracture | 116 | MPa | ASTM D638 |
| Fracture | 121 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.0 | % | ASTM D638 |
| Yield | 2.1 | % | ISO 527-2 |
| Fracture | 2.0 | % | ASTM D638 |
| Fracture | 2.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9650 | MPa | ASTM D790 |
| -- | 9000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 172 | MPa | ASTM D790 |
| -- | 176 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 7.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 640 | J/m | ASTM D4812 |
| 23°C 3 | 41 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.30 | J | ASTM D3763 |
| -- | 3.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 163 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 164 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 162 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 161 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 8.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 8.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 3.6E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 3.7E-5 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® EVA 1803 | Marco Polo International, Inc. | EVA | MARPOL® EVA |
| Sindustris PBT NH2307F | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Flexoprene® 65 | Puma Tecnica S.A.I.C.F.I | PE, Unspecified | Flexoprene® |
| Generic ETFE | Generic | ETFE | Generic |
| Kemcor HD 1155 | Qenos Pty Ltd | HDPE, HMW | Kemcor |