Bronze-filled epoxy for repairing, rebuilding, and maintaining bronze parts and equipment Intended Use:
Product features:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.23 | g/cm³ | |
| Specific Volume | 0.448 | cm³/g | |
| Solid content- by Volume | 100 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature Resistance | |||
| Dry | 121 | °C | |
| Wet | 49 | °C | |
| Tensile Shear Adhesion | 18.5 | MPa | ASTM D1002 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.10 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5520 | MPa | ASTM D638 |
| Flexural Strength | 42.6 | MPa | ASTM D790 |
| Compressive Strength | 58.9 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 5.9E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.66 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 0.98 | kV/mm | ASTM D149 |
| Dielectric Constant | 75.0 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 9.0 Mixing ratio by capacity: 3.0 | ||
| Component B | Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0 | ||
| Pot Life (24°C) | 35 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cured 7 days @ 75°F |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Curing Time | 16 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III PPJ1200 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| Shandong PA66 A2RG6301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 66 | Shandong PA66 |
| Nilac TR F17 V0 | Soredi S.p.a. | ABS | Nilac |
| Chemical Resources PET08012 | Chemical Resources, Inc. | PET | Chemical Resources |
| MARPOL® LL4M 820-G | Marco Polo International, Inc. | LLDPE | MARPOL® |