Celcon® GC15
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celcon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aUUSWX_Celcon-GC15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Celcon® GC15 is an acetal copolymer grade utilizing a nominal 15 wt. % fiber glass level to increase stiffness and strength. Chemical abbreviation according to ISO 1043-1: POM |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.54 | g/cm³ | ASTM D792 |
| -- | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.40 | % | ASTM D955 |
| Transverse flow | 1.8 | % | ASTM D955 |
| Vertical flow direction | 0.90 | % | ISO 294-4 |
| Flow direction | 0.50 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.80 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5950 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, 23°C | 85.5 | MPa | ASTM D638 |
| Fracture | 91.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 5850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.9 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 5.3 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 130 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 159 | °C | ISO 75-2/A |
| Melting Temperature | |||
| -- 1 | 166 | °C | ISO 11357-3 |
| -- | 165 | °C | ASTM D3418 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 4.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 190 | °C | |
| Front Temperature | 180 - 190 | °C | |
| Nozzle Temperature | 190 - 200 | °C | |
| Processing (Melt) Temp | 180 - 200 | °C | |
| Mold Temperature | 90.0 - 120 | °C | |
| Injection Pressure | 90.0 - 140 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 90.0 - 140 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 190 to 210°CZone 4 Temperature: 190 to 200°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TARFLON™ LZ2500V | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| TRIREX® Compound 3025GN10 | Samyang Corporation | PC | TRIREX® Compound |
| UNISOFT TPE™ ST-60A-BK-3-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| DOMAMID® 6B30 | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| Elastron® V V201.A40.N | Elastron USA, Inc. | TPV | Elastron® V |