DINALON® PA 6 30% CM
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupo Repol |
| Trademark: | DINALON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | aC4e90_DINALON-PA-6-30-CM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DINALON®PA 6 30% CM is a polyamide 6 (nylon 6) product, which contains a 30% mineral filler. It can be processed by injection molding and is available in Europe. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 75.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 3000 | MPa | ASTM D790 |
| Flexural Strength | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 55 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 190 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Glow Wire, UNE 20-672-83: 650°CVicat Softening Temperature, ASTM D1525: >190°CDTUL, ASTM D648: 110°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 246 | °C | |
| Mold Temperature | 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex A0050FB | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| ALCOM® PBT 700/12 PTFE10 | ALBIS PLASTIC GmbH | PBT | ALCOM® PBT |
| Fainplast PVC CKL 76/V | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| LNP™ THERMOCOMP™ DF0069P compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| Starex LX-9140 | LOTTE ADVANCED MATERIALS CO., LTD. | ASA | Starex |