Vyncolit® BXE7660
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a4uYri_VyncolitBXE7660.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® BXE7660 is a glass fiber reinforced phenolic molding compound with excellent mechanical properties and high temperature resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.84 | g/cm³ | ISO 1183 |
| Apparent Density | 0.59 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.14 | % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.060 | % | ISO 62 |
| Post Shrinkage | 0.040 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.2 | % | ISO 178 |
| Tensile Modulus | 19000 | MPa | ISO 527-2 |
| Tensile Stress | 101 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.68 | % | ISO 527-2 |
| Flexural Modulus | 18000 | MPa | ISO 178 |
| Flexural Stress | 210 | MPa | ISO 178 |
| Compressive Stress | 293 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.3 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 14 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 223 | °C | ISO 75-2/Af |
| 8.0 MPa, not annealed | 171 | °C | ISO 75-2/Cf |
| Linear thermal expansion coefficient | TMA | ||
| Flow | 1.4E-5 | cm/cm/°C | TMA |
| Lateral | 5.0E-5 | cm/cm/°C | TMA |
| Thermal Conductivity | 0.45 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.7E+13 | ohms | IEC 60093 |
| Volume Resistivity | 4.2E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.0 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell RP374R | LyondellBasell Industries | PP Random Copolymer | Purell |
| Sasol Polymers PVC S5718 | Sasol Polymers | PVC, Unspecified | Sasol Polymers PVC |
| Sindustris ABS LTR667 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| FHR Polypropylene P5C4K-089 | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| LNP™ THERMOCOMP™ UF006H compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |