TES J-50/30
| Category: | PC , Polycarbonate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | TES |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZuAoMB_TES-J-50-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Molding Parameters: 4 hours recommended for high tensile strength and smooth surface finish, or for vacuum metalizing. The dry temperature at 16 hours is 180°F. For 2-zone machines, the rear temperature is 600-650°F, and the front temperature is 580-620°F. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.090 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8270 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 134 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.5 | % | ASTM D638 |
| Flexural Modulus (23°C) | 7580 | MPa | ASTM D790 |
| Flexural Strength (Break, 23°C) | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 152 | °C | |
| 1.8 MPa, Unannealed | 143 | °C | |
| RTI Elec | UL 746 | ||
| 1.47 mm | 75.0 | °C | |
| 3.05 mm | 75.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.47 mm | 75.0 | °C | |
| 3.05 mm | 75.0 | °C | |
| RTI Str | UL 746 | ||
| 1.47 mm | 75.0 | °C | |
| 3.05 mm | 75.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.47 mm | V-2 | ||
| 3.05 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 299 to 316 | °C | |
| Middle Temperature | 310 to 343 | °C | |
| Front Temperature | 316 to 332 | °C | |
| Nozzle Temperature | 310 to 332 | °C | |
| Processing (Melt) Temp | 304 to 329 | °C | |
| Mold Temperature | 71.1 to 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Battery GPP1001M-P-2986 Grey | S&E Specialty Polymers, LLC | TPO | S&E Battery |
| Fainplast PVC RI 50 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Formolene® 2550A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| LNP™ LUBRICOMP™ RFL33 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| StarClear® 1035-0000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarClear® |