Hostaform® M15HP
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vc6gP2_Hostaform-M15HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostaform® acetal copolymer grade M15HP is a high viscosity polymer providing optimum performance in general purpose injection molding. This grade provides overall excellent performance in applications requiring high stiffness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 1.30 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.9 | % | ISO 294-4 |
| Flow direction | 2.3 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.75 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 68.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 16 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2750 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.5 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 240 | kJ/m² | ISO 179/1eU |
| 23°C | 280 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 158 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 101 | °C | ISO 75-2/A |
| Melting Temperature 1 | 173 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density of Melt | 1.170 | g/cm³ | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 190 - 200 | °C | |
| Middle Temperature | 190 - 210 | °C | |
| Front Temperature | 190 - 215 | °C | |
| Nozzle Temperature | 190 - 220 | °C | |
| Processing (Melt) Temp | 205 - 220 | °C | |
| Mold Temperature | 190 - 230 | °C | |
| Injection Pressure | 90.0 - 140 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 90.0 - 140 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 190 to 220°CZone 4 Temperature: 190 to 220°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer E70H | Precision Polymer Engineering Ltd. | EPDM | Precision Polymer |
| Sinelec CCB7824 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinelec |
| Karina IVORY PVC COMPOUND 900-35/2-P-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRILOY™ RF208 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |
| FRIANYL® B3 V0 | Nilit Plastics | Nylon 66 | FRIANYL® |