MARCOBLEND 2000 Sx Series
| Category: | PC , Polycarbonate |
| Manufacturer: | POLY GIN |
| Trademark: | MARCOBLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZpKFQU_MARCOBLEND-2000-Sx-Series.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MARCOBLEND 2000 Sx is a middle light-reflective ratio with 10% glass fiber content ignition resistant Polycarbonate resin. The resin is Halogen free and compliance with TCO and RoHS certification. The unique characters include superior processability, appropriate light- reflective efficacy and suitable for use in IT mechanical parts and optical parts which include notebook, LCD TV and Monitor back-light frame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 59.7 | MPa | ASTM D638 |
| Flexural Modulus | 2890 | MPa | ASTM D790 |
| Flexural Strength | 105 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 119 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow | 4.0E-5 | cm/cm/°C | |
| Transverse | 6.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Light Reflective Rate | 65 to 95 | % | ASTM E1104 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XYRON™ L654V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| NuSil MED-6381 | NuSil Technology | Silicone | NuSil |
| ALTECH® PA6 A 2030/320 GF30 UV | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| GETILAN ATP/190 X1 3A | Crosspolimeri S.p.A. | XLPE | GETILAN |
| Sylvin 9604-85 Clear Orange 5116 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |