ACCUTECH™ CP0436T10L
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | eiDxEx_ACCUTECH-CP0436T10L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™CP0436T10L is a polypropylene copolymer (PP Copoly) product, which contains 10% talc filler. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.948 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 62 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 23.0 | MPa | ASTM D638 |
| Fracture | 16.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | ASTM D638 |
| Fracture | 40 | % | ASTM D638 |
| Flexural Modulus | 1150 | MPa | ASTM D790 |
| Flexural Strength | 27.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 95 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 88.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 52.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 10% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR PP CONC 36 NAT S | PolyOne Corporation | PP, Unspecified | Maxxam™ FR |
| Tenite™ Propionate 380A4000015 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Versaflex™ FFC 2882-50 | PolyOne Corporation | TPE | Versaflex™ |
| KOPA® KN333HFBL | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| POCAN® BF 4409 000000 | LANXESS Corporation | PBT | POCAN® |