Vitaster® UX70BK6191
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | Vitaster® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zo4BNA_Vitaster-UX70BK6191.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vitaster® UX70BK6191 is a Polybutylene Terephthalate (PBT) product. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | 1.5 to 2.0 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 58.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Break | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength 1 | 3.00 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | 88.0 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength | 88 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 160 | °C | ASTM D648, ISO 75-2/B |
| Melting Temperature | 225 | °C | ASTM D2117, ISO 1218 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257, IEC 60093 |
| Comparative Tracking Index | |||
| Solution A | 225 | V | IEC 60112 |
| -- 3 | 225 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Oxygen Index | 30 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Method A |
| 3 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC G-4505 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Rotec® ASA T 115/03 | ROMIRA GmbH | ASA | Rotec® ASA |
| TECHNYL® A 246M BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| K-Flex 3370 OR | Technovinyl Polymers India Ltd. | PVC Elastomer | K-Flex |
| LNP™ LUBRICOMP™ RX05495 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |