Shinko-Lac® ABS SE-1
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Shinko-Lac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZmbOmr_Shinko-Lac-ABS-SE-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shinko-Lac ABS SE-1 is a high modulus grade of ABS that has superior extrusion processability as well as vacuum formability while maintaining a balance of rigidity, strength and glossiness. Typical applications of SE-1 include signboard, profile extrusion products and pipe. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 1.2 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2650 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 50.0 | MPa | ASTM D638 |
| Flexural Modulus (23°C, 6.35 mm) | 2750 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C, 6.35 mm) | 76.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.35 mm | 39 | J/m | |
| 0°C, 6.35 mm | 88 | J/m | |
| 23°C, 6.35 mm | 130 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 94.0 | °C | ASTM D648 |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1670 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 to 200 | °C | |
| Cylinder Zone 2 Temp. | 200 to 220 | °C | |
| Die Temperature | 190 to 220 | °C | |
| Take-Off Roll | 80.0 to 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBESTA 3030 JLX1 | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| LNP™ STAT-KON™ PD000 compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ STAT-KON™ |
| PLUSTEK RA304G6 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| Sylvin 8205-70UV Brown 7489 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| RONFALIN® ABS 1334 | A. Schulman Europe | ABS | RONFALIN® |