RTP 1899 A X 83675
| Category: | PC+Acrylic , Polycarbonate + Acrylic (PMMA) |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZhLg1V_RTP-1899-A-X-83675.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thin Wall Grade |
| General Information | |
|---|---|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.90 | % | ASTM D955 |
| Moisture Content | 0.020 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2070 | MPa | ASTM D638 |
| Tensile Strength | 49.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 74.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 1400 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D4812 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 238 - 266 | °C | |
| Mold Temperature | 32.2 - 65.6 | °C | |
| Injection Pressure | 55.2 - 82.7 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4005A TFE 10 | RTP Company | PPA | RTP |
| Reslen PPH 40T | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| Techsil 1387 BLACK | Techsil Limited | Silicone | Techsil |
| LAMINEX® 2010 | Schwartz Technical Plastic | PF | LAMINEX® |
| OP - PC/PBT 802-I | Oxford Polymers | PC+PBT | OP - PC/PBT |