LEXAN™ DMX3415M resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZdQG4K_LEXAN-DMX3415M-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN DMX3415M is a co-polycarbonate resin with improved scratch and abrasion resistance compared to standard polycarbonate. LEXAN DMX3415M is available in transparent colors. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.17 | g/cm³ | ISO 1183, ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 16.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.27 | % | |
| Equilibrium, 23°C, 50% RH | 0.13 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pencil Hardness 1 | H | ASTM D3363 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2900 | MPa | ASTM D638 |
| -- | 2450 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 80.0 | MPa | ASTM D638 |
| Yield | 80.0 | MPa | ISO 527-2/50 |
| Break 4 | 60.0 | MPa | ASTM D638 |
| Break | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 5 | 7.0 | % | ASTM D638 |
| Yield | 7.0 | % | ISO 527-2/50 |
| Break 6 | 36 | % | ASTM D638 |
| Break | 27 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 2600 | MPa | ASTM D790 |
| -- 8 | 2450 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 108 | MPa | ISO 178 |
| Yield, 50.0 mm Span 9 | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10 | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m² | |
| 23°C | 3.0 | kJ/m² | |
| Charpy Unnotched Impact Strength 11 | ISO 179/1eU | ||
| -30°C | 47 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 30 | J/m | ASTM D256 |
| 23°C | 30 | J/m | ASTM D256 |
| -30°C 12 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 13 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | No Break | ASTM D4812, ISO 180/1U | |
| -30°C 14 | 45 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 30.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 129 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 15 | 126 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 115 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 16 | 114 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 139 | °C | ASTM D1525 17 |
| -- | 134 | °C | ISO 306/B50 |
| -- | 136 | °C | ISO 306/B120 |
| CLTE | ASTM E831 | ||
| Flow : 23 to 80°C | 7.0E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 7.0E-5 | cm/cm/°C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.584 | ASTM D542, ISO 489 | |
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | < 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 280 to 305 | °C | |
| Front Temperature | 295 to 315 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Processing (Melt) Temp | 295 to 315 | °C | |
| Mold Temperature | 70.0 to 95.0 | °C |
| Note Message | |
|---|---|
| 1 . | 1 kgf |
| 2 . | 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | Type I, 50 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 sp=62mm |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 80*10*3 |
| 15 . | 80*10*4 mm |
| 16 . | 80*10*4 mm |
| 17 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1485 N | RTP Company | PESU | RTP |
| Westlake LDPE EF923 | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| Borflow™ HL508FB | Borealis AG | PP Homopolymer | Borflow™ |
| Elastane™ 4752-65D | Technical Polymers, LLC | TPU-Polyether | Elastane™ |
| Sylvin 8680-50D Clear 8359 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |