LNP™ STAT-KON™ OE008A compound
| Category: | PPS, Branched , Branched Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 2EAosI_LNP-STAT-KON-OE008A-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP STAT-KON OC-1008 is a compound based on PPS - Branched resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.050 to 0.25 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 179 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 0.70 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 30300 | MPa | ISO 178 |
| Flexural Stress | 290 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 25 | kJ/m² | ISO 180/1U |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+2 | ohms | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC P88023 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 800 GB 10 | RTP Company | Acetal (POM) Copolymer | RTP |
| SABIC® Vestolen A 5017 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| OmniPro™ CPP GRC50 | OMNI Plastics, LLC | PP Copolymer | OmniPro™ |
| PLANAC BT-2200-60 | TOYOBO America, Inc. | PBT | PLANAC |