Terblend® S NM-31
| Category: | ASA+Nylon , Acrylonitrile Styrene Acrylate + Nylon |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Terblend® S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZI2eZ9_Terblend-S-NM-31.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Terblend® S is a UV-stabilized ASA/PA blend with high impact strength, easy flow and pronounced color fastness. It is especially suitable for unpainted highly UV-exposed automotive interior parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (240°C/10.0 kg) | 60.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.80 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 3.3 | % | ISO 527-2 |
| Flexural Modulus | 2000 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation - MD (Break) | 25 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 70 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 92.0 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 205 | °C | ISO 306/A50 |
| -- | 110 | °C | ISO 306/B50 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 2.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.018 | IEC 60250 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE BM6246LS | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| SCHULAMID® 612 FS 5003 MC | A. Schulman Europe | Nylon 612 | SCHULAMID® |
| Sumitomo Phenolic XB-22 | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| SUPREME Specialty PS SP256 | Supreme Petrochem Ltd. | PS (Specialty) | SUPREME Specialty PS |
| Ultra Purge HT | Moulds Plus International USA, Inc. | Proprietary | Ultra Purge |