Lustran® ABS 433 is a general-purpose injection molding grade of ABS (Acrylonitrile Butadiene Styrene). It is a highimpact, high-gloss ABS, available only in natural (000000) and black (904000). In its natural color (000000), Lustran ABS 433 meets FDA requirements for food contact. Typical applications include housings, toys, small appliances, and consumer goods. As with any product, use of Lustran ABS 433 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 12 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2550 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 42.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 2620 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 64 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 370 | J/m | ASTM D256 |
| 23°C, 12.7 mm | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 12.7mm | 91.7 | °C | ASTM D648 |
| 0.45 MPa, annealed, 12.7mm | 99.4 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm, molded | 102 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 94.4 | °C | ASTM D648 |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 1 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 82.2 - 87.8 | °C | |
| B | 71.1 - 76.7 | °C | |
| Drying Time | |||
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Shot Size | 50 - 75 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 235 - 249 | °C | |
| Middle Temperature | 241 - 254 | °C | |
| Front Temperature | 246 - 260 | °C | |
| Nozzle Temperature | 246 - 260 | °C | |
| Processing (Melt) Temp | 246 - 274 | °C | |
| Mold Temperature | 43.3 - 65.6 | °C | |
| Injection Pressure | 68.9 - 110 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.172 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | 3.18 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Screw Speed: ModerateHold Pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sipolprene® 35150 B | SIPOL S.p.A | TPC-ET | Sipolprene® |
| THERMOLAST® K TF0STT (Series: FC/S) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Cevian®-V VGH10 | PlastxWorld Inc. | ABS | Cevian®-V |
| EMOPLEN® AT 1002 RT2 | EMAS Plastik San.Tic.AS. | PP, Unspecified | EMOPLEN® |
| PLUSTEK PA870G33 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |